API 5CT PSL1 K55 OCTG Tubing R2 9.3 LB Hot Rolled
Key Specifications / Features
Model No.: DB-OCTG Tubing-613 Hits: 34
China API 5CT PSL1 K55 OCTG Tubing Factory Derbo Provides API 5CT PSL1 K55 OCTG Tubing, Range 2, 9.3 LB, Hot Rolled, Oil and Gas Transportation.
Request a quote
Share
Tags:
Detail Information
Type: OCTG Tubing.
Standard and Material: API 5CT PSL1 K55.
Size: R2, 9.3 LB.
Manufacture Method: Hot Rolled.
Independence Inspection: Chemical Test, Mechanical Test.
Third Party Inspection: SGS, BV, INTERNET, etc.
Application: Oil and Gas Transportation.
Packing: Pallet/in Bundles or as Your Requirement.
Payment Terms: TT/LC, West Union, Paypal, O/A.
Delivery Time: 7-25 Days after Receiving the Deposit.
Standard and Material: API 5CT PSL1 K55.
Size: R2, 9.3 LB.
Manufacture Method: Hot Rolled.
Independence Inspection: Chemical Test, Mechanical Test.
Third Party Inspection: SGS, BV, INTERNET, etc.
Application: Oil and Gas Transportation.
Packing: Pallet/in Bundles or as Your Requirement.
Payment Terms: TT/LC, West Union, Paypal, O/A.
Delivery Time: 7-25 Days after Receiving the Deposit.
| Grade | Chemical Composition | ||||||||||||
| C | Mn | Mo | Cr | Ni | Cu | P | S | Si | |||||
| Min | Max | Min | Max | Min | Max | Min | Max | Max | Max | Max | Max | Max | |
| J55 | - | - | - | - | - | - | - | - | - | - | 0.03 | 0.03 | - |
| K55 | - | - | - | - | - | - | - | - | - | - | 0.03 | 0.03 | - |
| Mechanical Properties | ||||||||||||
| Grade | Yield Strength | Tensile Strength | Hardness | Allowable Hardness Variation | ||||||||
| Min | Max | Min | Max | |||||||||
| Psi | Mpa | Psi | Mpa | Psi | Mpa | HRC | BHN | hrc | ||||
| J55 | 55000 | 379 | 80000 | 552 | 75000 | 517 | - | - | - | |||
| K55 | 55000 | 379 | 80000 | 552 | 95000 | 655 | - | - | - | |||
| Lengths | |||||||||||||
| Description | Range 1 | Range 2 | Range 3 | ||||||||||
| Tubing | 6.10-7.32 M | 8.53-9.75 M | 11.58-12.80 M | ||||||||||
| Casing | 4.88-7.62M | 7.62-10.36 M | 10.36-14.63 M | ||||||||||
| Pup Joint | 0.5-6.0 M ( 2FT-20FT) | ||||||||||||